You are here: Home / PCM / Lauric acid (dodecanoic acid) / Enthalpy (T)

Enthalpy (T)

Measurement details

Measured with TA Q2000
By: ZAE Bayern
Additional Comments sample 3 of 3, subtraction of blank crucible was not necessary (signal of blank measurement negligible)
  • Heating rate1.0 [K/min]
  • Cooling rate1.0 [K/min]
  • Sample mass7.689 [mg]
  • Heat of fusion180.6 [kJ/kg] - deviation0.2 [kJ/kg]
    • Integration range, lower limit40.0 [°C]
    • Integration range, upper limit50.0 [°C]
    • Onset temperature43.4 [°C] - deviation0.0 [°C]
    • Offset temperature45.9 [°C] - deviation0.2 [°C]
  • Crystallization enthalpy185.4 [kJ/kg] - deviation0.2 [kJ/kg]
    • Integration range, lower limit33.0 [°C]
    • Integration range, upper limit43.0 [°C]
    • Onset40.0 [°C] - deviation0.2 [°C]
    • Offset39.2 [°C] - deviation0.3 [°C]
Enthalpy (T)

Set 1/ db-materials-heating_cooling_measurements

Heating - lauric-acid_sample3_heating1.txt

Cooling - lauric-acid_sample3_cooling1.txt

Set 2/ db-materials-heating_cooling_measurements-1

Heating - lauric-acid_sample3_heating2.txt

Cooling - lauric-acid_sample3_cooling2.txt

Set 3/ db-materials-heating_cooling_measurements-2

Heating - lauric-acid_sample3_heating3.txt

Cooling - lauric-acid_sample3_cooling3.txt