Enthalpy (T)

Measurement details

Measured with TA Q2000
By: ZAE Bayern
Additional Comments Sample 2 of 3. Integration range for crystallization enthalpy was 0 to 5 °C for cycles 1 and 2, and 5 to 10 °C for cycle 3.
  • Heating rate0.5 [K/min]
  • Cooling rate0.5 [K/min]
  • Sample mass12.785 [mg]
  • Heat of fusion134.4 [kJ/kg] - deviation0.2 [kJ/kg]
    • Integration range, lower limit25.0 [°C]
    • Integration range, upper limit40.0 [°C]
    • Onset temperature33.3 [°C] - deviation0.1 [°C]
    • Offset temperature35.3 [°C] - deviation0.1 [°C]
  • Crystallization enthalpy112.0 [kJ/kg] - deviation3.6 [kJ/kg]
    • Integration range, lower limit0.0 [°C]
    • Integration range, upper limit5.0 [°C]
    • Onset3.7 [°C] - deviation4.0 [°C]
    • Offset3.3 [°C] - deviation4.0 [°C]
Enthalpy (T)

Set 1/ db-materials-heating_cooling_measurements

Heating - CaBr2-6H2O_sample2_heating1.txt

Cooling - CaBr2-6H2O_sample2_cooling1.txt

Set 2/ db-materials-heating_cooling_measurements-1

Heating - CaBr2-6H2O_sample2_heating2.txt

Cooling - CaBr2-6H2O_sample2_cooling2.txt

Set 3/ db-materials-heating_cooling_measurements-2

Heating - CaBr2-6H2O_sample2_heating3.txt

Cooling - CaBr2-6H2O_sample2_cooling3.txt