You are here: Home / PCM / gypsum board / Enthalpy (T)

Enthalpy (T)

Measurement details

Measured with Setaram MicroDSCIII
By: Fraunhofer ISE
Additional Comments
  • Heating rate0.1 [K/min]
  • Cooling rate0.1 [K/min]
  • Sample mass391.12 [mg]
  • Heat of fusion19.22 [kJ/kg] - deviation0.1 [kJ/kg]
    • Integration range, lower limit10.0 [°C]
    • Integration range, upper limit25.0 [°C]
    • Onset temperature18.48 [°C] - deviation [°C]
    • Offset temperature24.08 [°C] - deviation [°C]
  • Crystallization enthalpy19.22 [kJ/kg] - deviation [kJ/kg]
    • Integration range, lower limit10.0 [°C]
    • Integration range, upper limit24.0 [°C]
    • Onset23.21 [°C] - deviation [°C]
    • Offset18.37 [°C] - deviation [°C]
Enthalpy (T)

Set 1/ db-materials-heating_cooling_measurements

Heating - Fraunhofer_ISE_gypsum_board_Sample3_Cycle1_0K1_min_Heating.dat

Cooling - Fraunhofer_ISE_gypsum_board_Sample3_Cycle1_0K1_min_Cooling.dat

Set 2/ db-materials-heating_cooling_measurements-1

Heating - Fraunhofer_ISE_gypsum_board_Sample3_Cycle2_0K1_min_Heating.dat

Cooling - Fraunhofer_ISE_gypsum_board_Sample3_Cycle2_0K1_min_Cooling.dat

Set 3/ db-materials-heating_cooling_measurements-2

Heating - Fraunhofer_ISE_gypsum_board_Sample3_Cycle3_0K1_min_Heating.dat

Cooling - Fraunhofer_ISE_gypsum_board_Sample3_Cycle3_0K1_min_Cooling.dat